NANOZR milling blank

NANOZR is a pre-sintered disk for dental CAD/CAM system developed by exploiting nanotechnology and has been backed by clinical research over 10 years.
NANOZR is a promising ceramics suitable for dental restorations required high structural strength because of its higher durability.

Ball drop impact test

Steel balls of 6, 14, 25 and 32 g were dropped from the 600 mm height onto the three kinds of 1 mm thick disks made of alumina, yttria-stabilized zirconia (Y-TZP) and NANOZR.
Alumina was easily broken at 6 g, whereas Y-TZP broke at 25 g. In contrast, NANOZR endured a weight of 32 g.

NANOZR

  • High fracture toughness in comparison with conventional zirconia
  • High bending strength
  • Resistance to Low Temperature Aging Degradation (LTAD)
  • High Weibull modulus (Indicates very homogeneous matrial)
  • Biocompatibility

ZrO2/Al2O3 - CERIA STABILIZED

Unique material properties offers safety

NANOZR is an intragranular type nanocomposite consisting zirconia matrix and alumina dispersions, which is reinforced with nano crystals. The physical properties of NANOZR are unique. NANOZR has a flexible property than that of conventional dental ceramics.
In addition, extremely high fracture toughness offers the best safety and reliability.
Furthermore, NANOZR has high resistant under hydrothermal conditions. Thus, NANOZR is applicable for various kinds of dental restorations.

Characteristics of NANOZR

Microstructure

NANOZR is a composite of Ceria stabilized Zirconia and Alumina. An intragranular nanostructure is obtained during sintering.

Physical properties

NANOZR is a unique material that combines much higher toughness and higher strength as compared to those of conventional zirconia. Crack length induced by Vickers indentation of NANOZR is quite shorter than that of other conventional ceramics.

Microstructure of NANOZR

Microstructure of NANOZR

Characteristics of NANOZR

Durability

NANOZR has a very high resistance to low temperature aging degradation (LTAD) under hydrothermal conditions.

Chemical solubility

NANOZR indicates no solubility in the oral environment.

Biocompatibility

NANOZR does not produce metallic allergy and has biological safety.

Optical micrograph around vickers indentation

Optical micrograph around vickers indentation ( Load : 490N )

Approach to structural strength analysis

As NANOZR possesses exclusive unique physical properties, it can apply various regions, such as thinner parts and/or complex shape which are required much higher strength. Panasonic proposes optimum shape design for newly intended application by taking advantage of our analysis and design technologies.

Approach to structural strength analysis

Case study of Stress Analysis

Case introduction by the customer

Case introduction by the customer
Case introduction by the customer

Return to Top

Product

NANOZR milling blank

Return to Top

Specifications

Specification

Trade name NANOZR milling blank
Diameter (mm) 98.3
Thickness (mm) 10, 12, 14, 16, 18, 20, 22, 25
Indications ex.) crown, bridge, etc.

Technical Data

Properties Measured Values Unit Standard Used
Density 5.52 g / cm³ JS R 1634
Bending strength 1290 MPa ISO 6872 (Biaxial)
Fracture toughness 8.62 MPam½ ISO 6872 (SEVNB)
CTE (25 ° C- 500 ° C) 10.0 10-6K-1 ISO 6872
Hardness 11.5 GPa JS R 1610 (Vickers)
Elastic modulus 245 GPa JS R 1602
Thermal conductivity 6.22 W / (mK) Laser Flash
Radioactivity 0.067 Bq / g ISO 6872
Chemical Solubility 0.00 μg / cm² ISO 6872

Return to Top

Quality Management

Quality Management

Panasonic is producing CAD/CAM blanks in house under consistent quality management ranging from raw materials to powder molding and pre-sintering, procedure and provides CAD/CAM blanks that customer can use in relief.

Dental prosthesis realizing high-precision fitting can be obtained because our CAD/CAM blanks are produced by using cold isocratic press (CIP), which makes possible to get isotropic shrinkage during full sintering procedure.

Panasonic Healthcare Co., Ltd. is certified in accordance with EN ISO 13485: 2003 / AC: 2009 and the Directive 93/42/EEC on Medical Devices (MDD).

Return to Top

PANASONIC HEALTHCARE NANOZR
AUTHORIZED MILLING CENTRES GERMANY

CADSPEED GmbH

Core 3d Centres Germany GmbH – Head Office

Core 3d Centres Berlin GmbH

Core 3d Centres München GmbH

DMC Cologne GmbH & Co. KG

Form for Function GmbH

Die Modellmacher oHG

Petersen Dental GmbH & Co. KG

R+K CAD/CAM Technologie GmbH & Co. KG

vFM Dentallabor GmbH

Wittenberg Dental Dr. Eikel

Zahntechnik Manfred Schmidt e.K.

DENMARKDENMARK

Solo-Tech Dental

ITALYITALY

LaStruttura S.p.A.

  • via Tintoretto 12, 21012 Cassano Magnago
  • Tel: +39 (0) 331-209434
  • Email: info@lastruttura.it
  • www.lastruttura.it

SWITZERLANDSWITZERLAND

Core 3d Centres Schweiz AG

Return to Top

Downloads

Contact Us

Direct inquiries regarding this product to the following.

Click here for the e-mail inquiry form.

Inquiry Form

Return to Top

Global Home Business > Healthcare > Products > You are here:NANOZR milling blank